The Impact of Gastric Juice on the Surface Roughness of Surface Sealant-Treated Provisional Restorations.

BACKGROUND AND AIM: Gastroesophageal reflux disease causes gastric acid to enter the oral cavity, leading to mucosal changes and deterioration of dental hard tissues and materials. The purpose of this in vitro study was to evaluate the impact of gastric juice on the surface roughness of two types of acrylics used in provisional restorations. MATERIALS AND METHODS: Acrytemp ® and Temdent acrylic resin discs (10 × 2 mm) totaling 80 were manufactured and divided into eight groups (n = 10). Groups were prepared as follows: Group 1 (Temdent + Universal Polish) (control), Group 2 (Temdent + Universal Polish + Biscover LV), Group 3 (Temdent + Universal Polish + Resin Glaze), Group 4 (Temdent + Universal Polish + Fortify Plus), Group 5 (Acrytemp + Universal Polish) (control), Group 6 (Acrytemp + Universal Polish + Biscover LV), Group 7 (Acrytemp + Universal Polish + Resin Glaze), and Group 8 (Acrytemp + Universal Polish + Fortify Plus). The resin discs were immersed in distilled water for 24 h and in gastric juice (pH = 2) for additional 24 h. The initial and final roughness values of samples were measured and analyzed with non-parametric statistics including Mann-Whitney U-test for pairwise comparison, Kruskall Wallis test for comparing more than two groups, and Wilcoxon signed rank test for within-group comparison (P < 0.05). RESULTS: Surface roughness did not differ significantly between control groups. It notably increased for all samples with surface sealants, both initially and after gastric juice immersion (P < 0.05). CONCLUSION: Surface sealants noticeably increased the roughness of two types of acrylic resins. After immersing in gastric juice, Group 4 (Temdent + Universal Polish + Fortify Plus) showed the highest roughness, while the untreated control groups remained the smoothest.

The Effect of Different Ageing Protocols on the Shear Bond Strength of the Ceromer Indirect Composite on Two Different Substructure Materials.

BACKROUND: The evolution of restorative materials in prosthodontics has led to the emergence of indirect composite resins, including ceromers, as alternatives to traditional metal-ceramic restorations. However, research gaps exist regarding the impact of ageing protocols on the bond strength of ceromer composites to different metal substructures, necessitating further investigation in this area. AIM: This study aimed to determine the effect of five different ageing protocols on the shear bond strength (SBS) of ceromer indirect composites on two different substructures. METHODS: In this in vitro study, 120 metallic discs (10 × 2 mm) were cast from cobalt-chromium (Co-Cr) alloy (n = 60) and spark erosion treated from grade V titanium (n = 60). Each sample was sandblasted. The M.L. primer (Shofu, Germany) and layers of opaque were applied to the surface following the manufacturer's instructions. A special jig (6 × 2 mm) was placed on each disc. The ceromer was condensed in it and light-cured separately for 90 s. Following polishing, specimens were separated into five ageing groups: distilled water (as a control), thermal cycling, tea, coffee, and gastric acid immersion. All samples were placed in 37°C incubation for 28 days for distilled water, coffee, and tea, and 7 days for gastric acid immersion and thermal cycling for 5000 cycles (5-55°C). A universal test machine was used to measure the SBS. The samples were evaluated for failure modes using stereomicroscopy. Data were analyzed using one-way analysis of variance (ANOVA) (P < 0.05). RESULTS: According to one-way ANOVA, the mean SBS (MPa) between the two groups was compared in each ageing protocol, and there were no significant differences between the Co-Cr-C and Ti-C groups (P > 0.05). The most frequent mode of failure in all groups was mixed. CONCLUSIONS: Applying the ageing protocols, the type of substructure material had no significant effect on the SBS of the ceromer indirect composite except for tea immersion.